Others Custom Made Solutions
Custom-made solutions involve
- R&D Cooperation
- Product Modification / Enhancement
- Toll Manufacturing
Waterborne Hardeners
Products | Amine Value (mg KOH/g) |
Viscosity (25°C, cPs) 1) |
Color (Gardner) |
Pot life (mins) 2) |
AHEW | Mix Ratio*3 (phr) |
Type | Solid Content % |
Properties / Applications |
---|---|---|---|---|---|---|---|---|---|
Jointmide 312 |
350 ± 20 |
4,000 ~ 7,000 |
<9 |
95 |
120 |
63 |
Self-Emulsifying Polyamide |
100 |
Bonding new concrete to old, wet surface adhesive |
Jointmide 3121 |
290 ± 20 |
25,000 ~ 45,000 |
<8 |
20 |
190 |
100 |
Self-Emulsifying Polyamide |
100 |
Cures in damp conditions. Bonding new concrete to old, damp concrete primer. |
Jointmide 3121-1 |
290 ± 20 |
4,000 ~ 7,000 |
<8 |
80 |
190 |
100 |
Self-Emulsifying Polyamide |
100 |
Water based primer for concrete, concrete curing compound, bonding new concrete to old |
Jointmide 3121-2 |
250± 20 |
500 ~ 1,000 |
<8 |
60 |
190 |
100 |
Self-Emulsifying Polyamide |
80 ± 2 |
Water based primer for concrete, concrete curing compound, bonding new concrete to old |
Jointmide 3121-4 |
200± 20 |
30,000 ~ 50,000 |
<12 |
62 |
280 |
150 |
Self-Emulsifying Polyamide |
50 ± 2 |
Water based primer for concrete, concrete curing compound, bonding new concrete to old |
Jointmide 3121-5 |
200± 20 |
25,000 ~ 50,000 |
<12 |
65 |
280 |
150 |
Self-Emulsifying Polyamide |
50 ± 2 |
Water based primer for concrete, concrete curing compound, bonding new concrete to old |
Jointmine 227 |
340 ± 20 |
1,500 ~ 3,500 |
<5 |
185 @200g |
100 |
50 |
Amine Adduct |
100 |
Semi-gloss coatings, self-levelling floor, wall coatings. |
Jointmine 4630 |
120 ± 20 |
15,000 ~ 35,000 |
<12 |
70 *4 |
280 |
150 |
Amine Adduct |
50 ± 2 |
Concrete sealers, primer, concrete floor and wall coatings |
Jointmine 4660 |
340 ± 20 |
8,000 ~ 16,000 |
<5 |
56 |
150 |
75 |
Amine Adduct |
100 |
Semi-gloss coatings, self-levelling floor, wall coatings. |
Jointmine 4661 |
300 ± 20 |
4,000 ~ 8,000 |
<5 |
46 |
170 ~ 190 |
75 |
Amine Adduct |
95 ± 2 |
Semi-gloss coatings, self-levelling floor, wall coatings. |
Modified Amines / Catalysts
Products | Amine Value (mg KOH/g) |
Viscosity (25°C, cPs) 1) |
Color (Gardner) |
Pot life (mins) 2) |
AHEW | Mix Ratio*3 (phr) |
Type | Properties / Applications |
---|---|---|---|---|---|---|---|---|
Jointmine NO.30 |
560 ~ 675 |
150 ~ 300 |
<8 |
- |
- |
5 ~ 10 *3 |
Tertiary Amine |
Catalyst for polyamines and polyamides. |
Jointmine NO.50 |
450 ~ 510 |
200 ~ 500 |
<3 |
- |
- |
3 ~ 5 *3 |
Accelerator |
Catalyst for polyamines and polyamides. |
Joint AH-501 |
- |
70 ~ 120 |
<2 |
- |
- |
80 ~ 100 *3 |
Anhydride |
Resistance to UV, light colored, outstanding mechanical and electrical characteristics. |
Joint AH-501-4 |
- |
50 ~ 110 |
<2 |
- |
- |
80 ~ 100 *3 |
Anhydride |
Resistance to UV, light colored, outstanding mechanical and electrical characteristics. |
Joint AH-502 |
- |
70 ~ 120 |
<6 |
- |
- |
85 ~ 100 *3 |
Anhydride |
Resistance to UV, light colored, outstanding mechanical and electrical characteristics. |
Joint 25UA
Joint 25UB |
- |
350 ~ 700 |
<2 |
6 ~ 7hrs *4 |
EEW 250 ~ 300 |
100 : 33 |
Modified Epoxy Resin |
High flexibility, transparent. Resists severe thermal and mechanical shocks. Pressure sensitive labels, high gloss dome & emblems |
270 ± 20 |
130 ~ 250 |
<2 |
AHEW 100 |
Modified Polyamine |
||||
Joint 27UA
Joint 27UB |
- |
350 ~ 700 |
<2 |
6 ~ 7hrs *4 |
EEW 250 ~ 300 |
100 : 33 |
Modified Epoxy Resin |
High flexibility, transparent. Resists severe thermal and mechanical shocks. Pressure sensitive labels, high gloss dome & emblems |
270 ± 20 |
150 ~ 250 |
<2 |
AHEW 100 |
Modified Polyamine |
||||
Joint EPU107A
Joint 105B |
- |
4,500 ~ 9,000 |
<4 |
48 |
EEW 650 ~ 750 |
100 : 20 |
Modified Epoxy Resin |
High degree of flexibility, eliminate moisture sensitivity, reduced epoxy brittleness, good UV resistance, resistance to low temperature |
370 ± 20 |
450 ~ 900 |
<4 |
AHEW 140 |
Modified Polyamine |
||||
Joint EPU107-5A
Joint 106B |
- |
1,500 ~ 4,500 |
<3 |
39 |
EEW 650 ~ 750 |
100 : 33 |
Modified Epoxy Resin |
High degree of flexibility, eliminate moisture sensitivity, reduced epoxy brittleness, good UV resistance, resistance to low temperature |
370 ± 20 |
30 ~ 60 |
<3 |
AHEW 140 |
Modified Polyamine |
2 Pot life in 100g mass at 25°C, minutes
3 phr: With Standard liquid Bisphenol A epoxy, EEW 182 ~ 192
4 Gel Time in 150g mass at 25°C